牌号简介 About |
---|
Vydyne® R530 NAT为通用型,注塑级,30%玻璃纤维增强PA66树脂。可在自然,它是良好的机器饲料,流动和模具释放润滑。 Vydyne R530 NAT is general-purpose, injection-molding grade, 30% glass-fiber reinforced PA66 resin. Available in natural, it is lubricated for good machine feed, flow and mold release. |
产品描述 Product Description
厂家:美国奥升德 Ascend
类别:PA66 PA66
用途:汽车的发动机罩下的零件;
颜色:自然色
加工条件:注射成型 Injection Molding
性能特点: 防火阻燃等级HB; 热稳定性好; 耐汽油; 耐化学性; 耐疲劳性好; 耐低温; 耐水解; 润滑性; 易流动; Good liquidity,Antifreeze,Solvent resistance,HB,Heat Stabilized,Fatigue resistance,Hydrolysis stability,Gasoline resistance,Lubricating
填料:玻璃纤维 30
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density Density |
1.37 | g/cm³ | ISO 1183 |
成型收缩率 Molding Shrinkage Molding shrinkage |
ISO 294-4 | ||
TD:23℃,2.0 mm TD:23℃,2.0 mm |
0.90 | % | ISO 294-4 |
MD:23℃,2.0 mm MD:23℃,2.0 mm |
0.40 | % | ISO 294-4 |
吸水率 Water Absorption Water Absorption |
|||
平衡 equilibrium,23℃,50% RH Balanced Equilibrium, 23 ℃, 50% RH |
1.9 | % | ISO 62 |
23℃,24hr 23℃,24hr |
0.90 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile Modulus Tensile Modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸强度 Tensile Strength Tensile Strength |
|||
断裂 brk,23℃ Broken BRK, 23 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile Strain Tensile Strain |
|||
断裂 brk,23℃ Broken BRK, 23 ℃ |
% | ISO 527-2 | |
弯曲模量 Flexural Modulus Flexural Modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 Flexural Strength Flexural Strength |
|||
23℃ 23℃ |
MPa | ISO 178 | |
泊松比 Poisson's ratio Poisson's ratio |
|||
23℃ 23℃ |
ISO 527 | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy notched Impact strength Charpy Notched Impact Strength |
ISO 179 | ||
-30℃ -30℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotched Impact strength Charpy Unnotch Impact strength |
ISO 179 | ||
-30℃ -30℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
悬臂梁缺口冲击强度 Izod Notched Impact strength Izod Notched Impact strength |
ISO 180 | ||
-30℃ -30℃ |
kJ/m² | ISO 180 | |
23℃ 23℃ |
kJ/m² | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT Hot deformation temperature HDT |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
熔融温度 Melting temperature Melting temperature |
℃ | ISO 11357-3 | |
线性热膨胀系数 Coeff.of linear therm expansion Coeff. of linear thermal expansion |
|||
TD:23~55℃,2 mm TD:23~55℃,2 mm |
1/℃ | ISO 11359-2 | |
MD:23~55℃,2 mm MD:23~55℃,2 mm |
1/℃ | ISO 11359-2 | |
相对温度指数 Relative Temp Index(RTI) Relative Temperature Index (RTI) |
|||
电气性能 Electrical performance |
UL 746 | ||
0.75 mm 0.75 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
UL 746 | ||
0.75 mm 0.75 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
UL 746 | ||
0.75 mm 0.75 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume Resistivity Volume Resistance |
|||
3.0 mm 3.0 mm |
ohms·cm | IEC 60093 | |
介电强度 Dielectric Strength Dielectric Strength |
|||
1 mm 1 mm |
kV/mm | IEC 60243 | |
耐电弧性 Arc Resistance Arc Resistance |
|||
3.0 mm 3.0 mm |
ASTM D495 | ||
相比漏电起痕指数 Comparative Tracking Index Compared Tracking Index |
|||
3.00 mm 3.00 mm |
V | IEC 60112 | |
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
0.75 mm 0.75 mm |
UL 746 | ||
1.5 mm 1.5 mm |
UL 746 | ||
3.0 mm 3.0 mm |
UL 746 | ||
高电压电弧起痕速率 High Voltage Arc Track Rate High Voltage Arc Track Rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot Wire Ignition Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
0.75 mm 0.75 mm |
UL 746 | ||
1.5 mm 1.5 mm |
UL 746 | ||
3.0 mm 3.0 mm |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating Flame Class Rating |
UL 94 | ||
0.75 mm 0.75 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
东芝扩建印度注塑机工厂
2016-01-05 日本东芝机械有限公司计划扩大其印度子公司的产能和产品范围,将生产1000吨以上的大型注塑机。 该公司将把钦奈工厂的产能从每年800台注塑机扩大到1000台以上,该公司告诉《塑料新闻》。 公司高管Girish Handigol表示,扩建将在未来三年内进行,已经购置了目前工厂隔壁的土地,以供扩建之需。 该公司还计划生产节能型和经济性系列,包括辅助系统。 该公司表示其印度业务的年增长率高达15%,高于10%的行业平均水平。 |
东芝扩建印度注塑机工厂 日本飞利浦机械设备有限责任公司计划扩张其印尼分公司的生产能力和商品范畴,将生产制造1000吨之上的大中型注塑机。 该企业将把钦奈工厂的生产能力从每一年800台注塑机扩张到1000台之上,该企业告知《塑料新闻》。 公司高管Girish Handigol表明,扩建将在未来三年内开展,早已购买了现阶段工厂邻居的土地资源,以供扩建之需。 该企业还计划生产制造环保型和合理性系列产品,包含輔助系统软件。 该企业表明其印尼业务流程的增长率达到15%,高过10%的领域平均。 扩建后的印尼工厂将生产制造最大达1800吨的塑料机械,现阶段那样的大载货量飞利浦设备只在日本生产制造。 该企业还表明,提产将能有利于提高抵抗中国注塑机的竞争能力。印度政府近期减少了对中国進口注塑机征缴的反补贴进口税率。 来源于:塑料新闻中国 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
加工方式 | |||
---|---|---|---|
注塑成型 Injection Molding | Dry | Unit | |
干燥温度 Drying Temperature | °C | ||
干燥时间 Drying Time | hr | ||
建议的最大回制料比例 Suggested maximum proportion of recycled materials | % | ||
后段温度 Rear Temperature -Zone 1 | °C | ||
中段温度 Middle Temperature -Zone 2 | °C | ||
前段温度 Front Temperature -Zone 3 | °C | ||
喷嘴温度 Nozzle Temperature | °C | ||
熔体温度 Melt Temperature | °C | ||
模具温度 Mold Temperature | °C |