牌号简介 About |
---|
Xenoy 1731树脂耐冲击/耐化学腐蚀。紫外线稳定。良好的物理性能保持在汽车外观和椭圆形。 Impact/chemical resistant. UV-Stabilized. Excellent physical property retention in automotive exteriors and OVAD. |
产品描述 Product Description
厂家:沙特沙伯基础 SABIC
类别:PC+PBT PC+PBT
用途:汽车外部零件;
加工条件:注射成型 Injection Molding
性能特点: 防火阻燃等级HB; 耐化学性; 冲击性能好; 耐候抗UV; Weather resistance is good,High impact resistance,Solvent resistance,HB
紫外线:UV Stabilized
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.22 | g/cm³ | ASTM D792 |
特定体积 Specific volume |
0.820 | cm³/g | ASTM D792 |
密度 Density |
1.22 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
250℃,5.0kg 250℃,5.0kg |
9.6 | g/10min | ASTM D1238 |
250℃,5.0kg 250℃,5.0kg |
8.0 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
TD:3.2 mm TD:3.2 mm |
% | 内部方法 | |
MD:3.2 mm MD:3.2 mm |
% | 内部方法 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2/50 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
屈服 yield 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain 3 |
|||
断裂 fracture 4 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
屈服 yield |
% | ISO 527-2/50 | |
屈服 yield 3 |
% | ASTM D638 | |
弯曲模量 Bending modulus 5 |
MPa | ISO 178 | |
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength 5 , 6 |
MPa | ISO 178 | |
弯曲强度 bending strength 4 |
|||
屈服,50 mm跨度 Yield, 50 mm span 4 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 7 |
|||
23℃ 23℃ 7 |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
23℃,6.4mm 23℃,6.4mm |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 8 |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
ASTM D3763 | ||
-30℃,Total Energy -30℃,Total Energy |
J | ASTM D3763 | |
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 9 |
℃ | ISO 75-2/Af | |
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 10 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ISO 11359-2 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ISO 11359-2 | |
MD MD |
ASTM E831 | ||
-40 到 40℃ -40 to 40 ℃ |
cm/cm/℃ | ASTM E831 | |
-40 到 95℃ -40 to 95 ℃ |
cm/cm/℃ | ASTM E831 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
耐电弧性 Arc resistance 11 |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50 mm 1.50 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.20 in/min |
3 类型 1, 2.0 in/min |
4 0.051 in/min |
5 0.079 in/min |
6 Yield |
7 80*10*4 sp=62mm |
8 80*10*4 |
9 80*10*4 mm |
10 标准 B (120°C/h), 载荷2 (50N) |
11 钨电极 |
【新闻资讯】查看全部
国际石油公司将注意力转向绿色氢能源
2022-03-13 据烃加工新闻3月3日消息称,GlobalData 表示,领先的国际石油公司正在重组其业务,以采用低碳氢等新的能源转型技术,成为综合能源供应商。这家领先的数据分析公司指出,随着人们对 |
国际石油公司将注意力转向绿色氢能源 据烃加工新闻3月3日消息称,GlobalData 表示,领先的国际石油公司正在重组其业务,以采用低碳氢等新的能源转型技术,成为综合能源供应商。这家领先的数据分析公司指出,随着人们对氢的兴趣增加,一些大型综合性石油公司迄今为止宣布了生产低碳氢超过290万吨/年的项目。 GlobalData 能源转型分析师 Barbara Monterrubio 评论说:“一些公司比其他公司行动更快、更果断,现在正在增加主要在绿色氢生产方面的投资。这是由于他们对脱碳的承诺,以及未来从氢经济的预期增长中获得的潜在利益。” 根据GlobalData的报告“油气中的氢-专题研究”,为了实现业务组合的脱碳,各公司已经开始投资绿色氢项目的开发,87%的管道产能来自这些项目。 Monterrubio继续说道:“为了支持绿色氢经济,国国际石油公司也在据称的氢经济的其他方面改善了他们的足迹。他们通过投资燃料电池技术、燃料补给网络和氢储存来创造能源领域的替代收入来源。此外,欧洲一体化企业也在迅速投资于清洁能源领域。” 炼油和化工行业占了现有氢需求的大部分。低碳氢项目可以帮助石油和天然气公司自身运营的脱碳工作。利用氢作为化工行业生产低碳氨和甲醇的关键原料,以及开发生物燃料,将是石油和天然气行业对氢的需求不断增加的领域。 Monterrubio 补充说:“交通和电力等其他行业的氢需求有可能迅速增长。氢作为传统燃料的清洁燃烧替代品的潜力使其成为一个很好的替代品,因为石油和天然气行业可以利用其资产在不断发展的氢经济中获益。” |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
原厂数据及认证:
抱歉!该牌号暂无认证数据。
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情